TGA@9531 Poly-Asparagus Poly-Asparagus Antisepsis Coating Material
【Product Manual】
Product Description
TGA9531 is formed by the reaction polymerization of polyaspartic acid ester and polyisocyanate. Because polyaspartic acid ester is aliphatic hindered secondary amine, and the curing component
is aliphatic polyisocyanate, the film formed has high light and color retention characteristics, and the bottom, middle and surface are integrated, which is suitable for long-term outdoor use. When
secondary amine groups react with isocyanate groups, a high cross-linking density and interpenetrating polymer chain network structure is formed, which also makes this product have good physical
and chemical characteristics.
Product Features And Advantages
1.High solid and low viscosity, good leveling property, tough and dense coating, plump and bright, and bright color.
2.Strong adhesion to the base, and good compatibility with polyurethane, epoxy and other materials.
3.High hardness, good scratch resistance and stain resistance.
4.Excellent wear resistance and impact resistance.
5.Excellent corrosion resistance and chemical medium resistance, such as acid, alkali, salt and so on.
6.No discoloration, yellowing, pulverization, aging resistance, excellent weather resistance and light and color retention.
7.It can be directly applied to surface coating of metal surface (DTM).
8.This product does not contain benzene solvents and lead elements, and is environmentally friendly.
Recommended Use
Corrosion protection and protection of steel structures, storage tanks, containers, valves, natural gas pipelines, frames, axles, shelves, tank cars, swimming pools, sewage pools, various wear-resistant
floor surfaces, terrazzo surfaces, chemical cofferdams and other fields.
Product Information
Physical Properties Of Product
Product Corrosion-Resistant Medium
Product Construction Environment
Method Of Application
Hand brushing and rolling brush
Two-component variable ratio high-pressure airless spraying machine
Recommended dry film thickness: 200-500μm m.
Coating interval: minimum 0.5h and maximum 24h.
Points For Attention
Before use, mix the component B thoroughly and evenly.According to the requirements, the mixture ratio is adjusted, and how much is used, and it is used after being stirred evenly. The prepared coating
is used up within 30 minutes.After painting, the raw materials in the packaging barrel must be tightly covered to prevent moisture absorption.Keep it dry and clean during construction, and do not contact
with water, alcohol, acid, alkali, etc.
Curing Time
Product Shelf Life
1. Storage environment temperature: 5℃-35℃.
2. The shelf life of the product shall start from the production date and be in the unopened state.
3. component A: 10 months; component B: 10 months.
4. Make sure that the product packaging is well sealed.
5. Store in a cool and ventilated environment to avoid direct sunlight.
6. Packaging: 9 kg/barrel for component A and 21 kg/barrel for component B.
Product Health And Safety Information
Please refer to the latest version of the product technical safety technical instruction manual (MSDS) of Aochang Company for information and suggestions on product operation, storage and disposal. It includes product physical characteristics, ecological, toxicological data and other related safety information data.
Statement Of Good Faith
AoChang promises that all the product data listed above are obtained by testing in relevant laboratories according to corresponding standards. During the test, the relevant data will be slightly different due to the different test environment and methods. Therefore, AoChang company advises customers to do experimental demonstration before using the product. Except for the product quality itself, AoChang Company assumes no responsibility and reserves the right to adjust and update the above data without prior notice.